One-pot solvothermal synthesis of highly emissive, sodium-codoped, LaF3 and BaLaF5 core-shell upconverting nanocrystals

Abstract

We report a one-pot solvothermal synthesis of sub-10 nm, dominant ultraviolet (UV) emissive upconverting nanocrystals (UCNCs), based on sodium-codoped LaF3 and BaLaF5 (0.5%Tm; 20%Yb) and their corresponding core@shell derivatives. Elemental analysis shows a Na-codopant in these crystal systems of ~20% the total cation content; X-ray diffraction (XRD) data indicate a shift in unit cell dimensions consistent with these small codopant ions. Similarly, X-ray photoelectron spectroscopic (XPS) analysis reveals primarily substitution of Na+ for La3+ ions (97% of total Na+ codopant) in the crystal system, and interstitial Na+ (3% of detected Na+) and La3+ (3% of detected La3+) present in (Na)LaF3 and only direct substitution of Na+ for Ba2+ in Ba(Na)LaF5. In each case, XPS analysis of La 3d lines show a decrease in binding energy (0.08–0.25 eV) indicating a reduction in local crystal field symmetry surrounding rare earth (R.E.3+) ions, permitting otherwise disallowed R.E. UC transitions to be enhanced. Studies that examine the impact of laser excitation power upon luminescence intensity were conducted over 2.5–100 W/cm2 range to elucidate UC mechanisms that populate dominant UV emitting states. Low power saturation of Tm3+ 3F3 and3H4 states was observed and noted as a key initial condition for effective population of the1D2 and1I6 UV emitting states, via Tm-Tm cross-relaxation.