Residual tensile strength of the multi-impacted scarf-repaired glass fiber-reinforced polymer (GFRP) composites

Abstract

The effect of multiple/repeated impacts on a repaired composite was investigated using a low-velocity impact test. The composite samples were fabricated through a vacuum resin infusion method (VARI) and repaired by a scarf repair technique. Later, a repeated low-velocity impact test was performed on the original and repaired composites samples. Performance of the multi-impacted repaired and original samples was evaluated and compared by measuring maximum contact force, maximum displacement, maximum time duration, absorbed energy and damage area. Photographs of the post-impacted samples were taken to observe the multi-impact damage progression through visual inspection. The results showed that each repeated impact subjected the samples to more damage. Tensile tests revealed that the scarf repair restored 81.23% strength. It was also observed that the sample obtained the highest damage dent in the low-velocity impact test that failed early during a tensile test and carried the lowest ultimate load.