Hygrothermal deterioration in carbon/epoxy and glass/epoxy composite laminates aged in marine-based environment (degradation mechanism, mechanical and physicochemical properties)

37Citations
Citations of this article
38Readers
Mendeley users who have this article in their library.

This article is free to access.

Abstract

One of the major challenges in off-shore tidal and wave energy devices is the ageing of these structures in the hostile marine environment, which limits their operating life. In this research, mechanical properties of aged glass/epoxy and carbon/epoxy composite specimens including tensile strength, Young’s modulus, flexural strength, and shear strength, following immersion in a representative accelerated marine degradation environment (artificial seawater, with 3.5% salinity at room temperature and 60 °C) have been investigated. The microstructure and physicochemical characterization of the aged samples were assessed via microscopic imaging, micro-CT scanning and differential scanning calorimetry. The degradation phenomenon was apparent in the change of mechanical properties and microstructure of composite laminates (micro-cracks and debonding between matrix and fibre). Generally, the ageing process had a more severe effect on tensile and shear strengths of glass/epoxy samples than those of carbon/epoxy specimens. Reversely, the results of bending tests of carbon/epoxy composites showed more drop-in flexural properties than glass/epoxy samples. The results revealed that degradation mechanisms continue even after reaching the saturation point in composite materials. The achievements of this research present a good understanding of the effect of degradation of composite materials in salt water to deal with their application in real service environment.

Cite

CITATION STYLE

APA

Ghabezi, P., & Harrison, N. M. (2022). Hygrothermal deterioration in carbon/epoxy and glass/epoxy composite laminates aged in marine-based environment (degradation mechanism, mechanical and physicochemical properties). Journal of Materials Science, 57(6), 4239–4254. https://doi.org/10.1007/s10853-022-06917-2

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free