Photoelectrochemical performance of NiO-coated ZnO-CdS core-shell photoanode

22Citations
Citations of this article
45Readers
Mendeley users who have this article in their library.

This article is free to access.

Abstract

A nano-structured core-shell ZnO-CdS photoanode device with a mesoporous NiO co-catalyst layer was fabricated using solution-processing methods. The growth of the sparse ZnO nano-rod film with a thickness of ca. 930 nm was achieved by optimizing parameters such as the thickness of the ZnO seed layer, choice of Zn precursor salt and the salt concentration. CdS was then coated by a combination of spin coating and spin SILAR (Successive Ionic Layer Adsorption and Reaction) methods to completely fill the interspace of ZnO nano-rods. The uniform CdS surface facilitated the growth of a continuous mesoporous NiO layer. Upon illumination of 100 mW•cm-2 AM 1.5 G radiation the device exhibits stable photocurrents of 2.15 mA•cm-2 at 1.23 V and 0.92 mA•cm-2 at 0.00 V versus RHE, which are significantly higher as compared to the bare ZnO-CdS device. The excellent performance of the device can be ascribed to the higher visible region absorption by CdS, and effective separation of the photogenerated charge carriers due to the suitable band alignment and nanostructuring. Additionally, the mesoporous NiO overlayer offered a larger contact area with the electrolyte and promoted the kinetics enabling higher and stable photocurrent even till the 35th min. of testing.

Cite

CITATION STYLE

APA

Iyengar, P., Das, C., & Balasubramaniam, K. R. (2017). Photoelectrochemical performance of NiO-coated ZnO-CdS core-shell photoanode. Journal of Physics D: Applied Physics, 50(10). https://doi.org/10.1088/1361-6463/aa5875

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free