In-Operando Anomalous Small-Angle X-Ray Scattering Investigation of Pt 3 Co Catalyst Degradation in Aqueous and Fuel Cell Environments

Abstract

Platinum-cobalt alloy nanoparticles are of great interest as cathode catalysts for PEMFCs as they have been shown to have enhanced activity versus platinum. However, their relative stability against loss of electrochemically-active surface area in relation to Pt catalysts is still debated. In this study, the evolutions of Pt 3 Co particle size distributions (PSDs) in fuel cell and aqueous environments were fol-lowed during accelerated stress tests (ASTs) using in-operando ASAXS. The measured evolutions showed a degradation mechanism dominated by loss of particles smaller than the critical particle diameter (<5.2 to 6.1 nm, CPD), which depended on environment and the AST. These evolutions were compared to that of a Pt catalyst with a similar initial PSD, which was found to have a lower degrada-tion rate than Pt 3 Co. The ASAXS data, as well as data from aqueous dissolution, X-ray absorption spectroscopy, individual particle energy-dispersive spectroscopy, X-ray fluorescence spectrometry, and kinetic Monte Carlo calculations support a loss mechanism of increased Pt dissolution from Pt 3 Co versus Pt due to destabilization caused by extensive dealloying of particles