Investigation of the Impact of an Electric Field on Polymer Electrolyte Membranes for Fuel Cell Applications

Abstract

A systematic study was carried out on Nafion® 112 membranes to evaluate the effects of different electric field strengths on the structural and electrical properties of the membranes. The membranes were subjected to different electric field strengths (0, 40, 80, and 140 MV/m) at a temperature of 90 °C. Proton conductivity was measured using an LCR meter, revealing that conductivity values varied with the electric field strengths, with the optimal conductivity observed at 40 MV/m. Positron annihilation lifetime (PAL) spectroscopy provided insights into the free volume structure of the membranes, showing an exponential increase in the hole volume size as the electric field strength increased. It was also found that the positronium intensity of the Nafion® 112 membranes was influenced by their degree of crystallinity, which decreased with higher electric field strengths. This indicates complex interactions between structural changes and the effects of the electric field. Dielectric studies of the membranes were characterized over a frequency range of 50 Hz to 5 MHz, demonstrating adherence to Jonscher’s law. The Jonscher’s power law’s s-parameter values increased with the electric field strength, suggesting a transition from a hopping conduction mechanism to more organized ionic transport. Overall, the study emphasizes the relationship between the free volume, crystallinity, and macroscopic characteristics, such as ionic conductivity. The study highlights the potential to adjust membrane performance by varying the electric field.