Preparation and characterization of fast-curing powder epoxy adhesive at middle temperature

Abstract

At present, the disadvantage of powder epoxy adhesive is the limited application area. In order to widen the application range of powder epoxy adhesive from heat-resistant substrates (such as metals) to heat-sensitive substrates (such as plastic products, cardboard and wood), it is necessary to decrease the curing temperature. In this article, a series of fast-curing powder epoxy adhesives were prepared by the melt blending method with bisphenol A epoxy resin (E-20), hexamethylenetetramine (HMTA) as a curing agent and 2-methylimidazole (2-MI) as an accelerant. The structure and properties of the E-20/HMTA/2-MI systems were characterized by Fourier transform infrared, thermogravimetric analysis, dynamic mechanical analyser and differential scanning calorimetry (DSC). 2-MI added into the E-20/HMTA systems can simultaneously enhance toughness, tensile strength, glass transition temperature (Tg) and thermal stability in comparison with the E-20/HMTA systems. The best mechanical properties were obtained at 100/8/0.6 weight ratio of the E-20/HMTA/2-MI systems. DSC experiments revealed that the exothermic peak of the E-20/HMTA/2-MI system was about 558C lower than that of the E-20/HMTA system. The activation energy of the cure reaction was determined by both Kissinger's and Ozawa's methods at any heating rates. The activation energy and pre-exponential factor were about 100.3 kJ mol21 and 3.57 1011 s21, respectively. According to the KAS method, the curing time of the E-20/HMTA/2-MI systems was predicted by evaluating the relationship between temperature and curing time.