A Study on the Charging–Discharging Mechanism of All Solid-State Aluminum–Carbon Composite Secondary Batteries

Abstract

Aluminum solid-state batteries are emerging as one of the most promising energy storage systems, offering advantages such as low cost and high safety. This study adopts a safe and cost-effective approach by alloying and doping the all-solid-state aluminum-ion battery to enhance its electrochemical performance. This research further explores the electrochemical impacts of these modifications on the performance of solid-state aluminum batteries. In this experiment, aluminum-based anodes were deposited onto nickel foil using the thermal evaporation (TE) method. At the same time, the graphite film (GF) cathode material was enriched with sodium (GFN) through a solution-based process. The system was combined with magnesium silicate solid electrolytes to investigate the all-solid-state aluminum-carbon battery′s structural characteristics and charge–discharge mechanisms. The experimental results demonstrate that the aluminum-coated electrode alloying effects and the graphite film modification significantly improve battery performance. The system achieved a maximum specific capacity of approximately 700 mAh g−1, with a cycle life exceeding 100 cycles. Furthermore, the microstructural characteristics and phase structure of the aluminum evaporation film were confirmed. Analysis of ion transport pathways during the charge–discharge cycles of the all-solid-state aluminum-carbon battery revealed that both aluminum and magnesium ions play critical roles in the electrode processes.