The Morphology Analysis of Plasma-Sprayed Cast Iron Splats at Different Substrate Temperatures via Fractal Dimension and Circularity Methods

Abstract

Plasma-sprayed cast iron splats were deposited onto polished aluminum substrates preheated to different temperatures ranging from 25°C to 250°C. The morphology of single splat was observed by a field emission scanning electron microscope. Quantitative characterization methods, including fractal dimension (FD) and circularity analyses of the splat profile, were employed to identify the difference in morphology of the splats with the change of the substrate temperature. The results showed that the substrate temperature has a significant effect on the spreading of molten droplets and the morphology of resultant splats through changing the solidification rate of the droplets. With the increment of substrate temperature, the homogeneous and sufficient spreading of the droplets resulted from low solidification rate reduces the splashing of the droplets. In addition, the evaporation of adsorbed moisture on the substrate improves the wettability between the spreading droplet and the substrate, then benefits the homogeneous spreading of the molten droplet. As a result, a distinct decline in the FD value was observed. It was also suggested that the FD analysis could be used to characterize the morphology of the splat more effectively while the circularity method was heavily dependent on the area of the splat.