Characterization of magnetite (Fe3O4) minerals from natural iron sand of Bonto Kanang Village Takalar for ink powder (toner) application

Abstract

This research is about magnetite's characterization (Fe3O4) from natural iron sands of Bonto Kanang Village, District of Takalar for ink powder (toner) application. This study aims to determine the process parameters to obtain magnetite of high purity degree and to observe its physical characteristics as a supporting toner material which synthesized through co-precipitation method. The iron sand was first separated by the magnetic technique and dissolved into HCl solution before conducting the precipitation process. Precipitation was done by dripping ammonium hydroxide (NH4OH). The precipitated powder was dried at 100°C, and then calcined at 400°C. The purity degree and magnetite mineral grain size were analyzed by XRD and SEM-EDS. The EDS elemental test before and after precipitation shown an increase of iron oxide composition from 66.70% to 87.76%. Diffractogram of XRD before and after precipitation showed Fe3O4 compounds with magnetite phase of 59% and 98%, respectively. The crystal structure iron sand powder structure before and after precipitation is cubic with each lattice parameters a = b = c = 8.384971 Å, V = 589.528423 Å3 and a = b = c = 8.386829 Å and V = 589.920291 Å3 when angle α = β = γ = 90°. SEM images (using SE and HV 20kV) showed inhomogeneous magnetite morphology. The magnetite phase percentage that obtained based on the XRD analysis gives information that magnetite precipitation has been successfully performed with high degree of purity. The material obtained can be applied as a support toner material.