Characterization of Ga2Se3 at ZnSe/GaAs heterovalent interfaces

Abstract

Despite the valence difference across the junction, it has been shown that ZnSe/GaAs epilayer/epilayer interface state densities can be reduced to values comparable to the (Al,Ga)As/GaAs interface. We have previously reported a transmission electron microscopy study indicating that ZnSe/GaAs structures exhibiting low interface state densities are associated with the formation of an interfacial layer of zinc-blende Ga2Se3. In this letter we describe a procedure whereby an interfacial layer can be deliberately introduced prior to nucleation of ZnSe. In situ x-ray photoelectron spectroscopy is used to study the nature of the bonding at the interfacial layer. A comparison of the Se 3d core level features from the ZnSe epilayer surface, a Se-reacted GaAs surface, and from a separately grown Ga2Se 3 epilayer, clearly indicates the same Se bonding characteristic for the Se-reacted interfacial layer and the Ga2Se3 epilayer.