Evaporated mapbi3 perovskite planar solar cells with different annealing temperature

Abstract

The power conversion efficiency (PCE) of an Ag/spiro-OMeTAD/CH3 NH3 PbI3 (MAPbI3)/ PCBM/mesoporous TiO2 /compact TiO2 /FTO planar solar cell with different annealing temperatures of PbI2 and MAPbI3 films was investigated in this study. The morphology control of a MAPbI3 thin film plays key roles in high-efficiency perovskite solar cells. The PbI2 films were prepared by using thermal vacuum evaporation technology, and the MAPbI3 perovskite films were synthesized with two-step synthesis. The X-ray spectra and surface morphologies of the PbI2 and MAPbI3 films were examined at annealing temperatures of 80, 100, 120, and 140◦ C for 10 min. The performance of the perovskite planar solar cell at an annealing temperature of 100◦ C for 10 min was demonstrated. The power conversion efficiency (PCE) was about 8.66%, the open-circuit voltage (Voc) was 0.965 V, the short-circuit current (Jsc) was 13.6 mA/cm2, and the fill factor (FF) was 0.66 by scanning the density–voltage (J–V) curve.