Large-Scale Production of Carbon-Supported Cobalt-Based Functional Nanoparticles for Oxygen Evolution Reaction

Abstract

A series of Co-based nanoparticles supported on activated carbon was synthesized by using waste tea leaves as a template as well as a sustainable carbon source. The crystal structure of the Co particles was adjusted by post-treatments with H2O2, ethanol vapor, and H2, which result in Co3O4, CoO, and metallic Co phases, respectively. After these different treatments, the composite materials consist of small Co-based nanoparticles with an average crystallite size of 6–14 nm supported on activated carbon with apparent specific surface areas up to 1065 m2 g−1. Correlations between the structure of the materials and their activity for the oxygen evolution reaction (OER) were established, whereby the post-treatment with ethanol vapor was found to yield the most effective electrocatalyst. The material shows good stability at 10 mA cm−2 over 10 h and reaches a mass activity of 2.9 A mgCo−1, which is even higher than pristine ordered mesoporous Co3O4. The superior electrocatalytic performance is ascribed to a high dispersion of Co-based nanoparticles and the conductivity of the activated carbon that facilitate the charge transport.