Mn-doped Co3O4 for acid, neutral and alkaline electrocatalytic oxygen evolution reaction

Abstract

This work reports the application of Mn-doped Co3O4 oxides in the electrocatalytic oxygen evolution reaction (OER). The materials were characterized by structural, morphological, and electrochemical techniques. The oxides with higher Co : Mn molar ratio presented a lower electron transfer resistance, and consequently the most promising OER activities. Pure Co3O4 shows an overpotential at j = 10 mA cm−2 of 761, 490, and 240 mV, at pH 1, 7, and 14, respectively, and a high TOF of 1.01 × 10−1 s−1 at pH 14. Tafel slopes around 120 mV dec−1 at acidic pH and around 60 mV dec−1 at alkaline pH indicate different OER mechanisms. High stability for Co3O4 was achieved for up to 15 h in all pHs, and no change in the structure and morphology after the electrocatalysis was observed. The reported excellent OER activity of the Mn-Co oxides in a wide pH range is important to broaden the practical applicability in different electrolyte solutions.