Properties of TiC and TiN reinforced alumina–zirconia composites sintered with spark plasma technique

Abstract

In this paper, Al2 O3 –ZrO2 composites with an addition of 20 wt% TiN and 10 wt% TiC were modified. The addition of zirconia in a range from 2 to 5 wt% of the monoclinic phase and 10 wt% of Y2 O3 stabilised ZrO2 affected the mechanical properties of the composites. A new type of sintering technique—the spark plasma sintering (SPS) method—within a temperature range from 1575◦ C to 1675◦ C, was used. Vickers hardness, apparent density, wear resistance and indentation fracture toughness KIC(HV) were evaluated at room temperature. An increase of the sintering temperature resulted in an improvement of Vickers hardness and an increase of the fracture toughness of the tested composites. The tribological properties of the samples were tested using the ball-on-disc method. The friction coefficient was in a range from 0.31 to 0.55, depending on the sintering temperature. An enhancement of the specific wear rate was dependent on the sintering temperature. The mechanical properties of the samples sintered by pressureless sintering (PS) were compared. X-ray diffraction patterns were presented in order to determine the phase composition. SEM microstructure of the tested composites sintered at different temperatures was observed.