A novel zirconia-based composite presents an aging resistant material for narrow-diameter ceramic implants

Abstract

A novel ceria-stabilized zirconia-alumina-aluminate composite (Ce-TZP-comp) that is not prone to aging presents a potential alternative to yttrium-stabilized zirconia for ceramic oral implants. The objective of this study was to evaluate the long-term stability of a one-piece narrow-diameter implant made of Ce-TZP-comp. Implant prototypes with a narrow (3.4 mm) and regular (4.0 mm) diameter were embedded according to ISO 14801, and subgroups (n = 8) were subsequently exposed to dynamic loading (107 cycles, 98N) and/or hydrothermal treatment (aging, 85◦C). Loading/aging was only applied as a combined protocol for the 4.0 mm diameter implants. One subgroup of each diameter remained untreated. One sample was cross-sectioned from each subgroup and evaluated with a scanning electron microscope for phase-transformation of the lattice. Finally, the remaining samples were loaded to fracture. A multivariate linear regression model was applied for statistical analyses (significance at p < 0.05). All samples withstood the different loading/aging protocols and no transformation propagation was observed. The narrow diameter implants showed the lowest fracture load after combined loading/aging (628 ± 56 N; p < 0.01), whereas all other subgroups exhibited no significantly reduced fracture resistance (between 762 ± 62 and 806 ± 73 N; p < 0.05). Therefore, fracture load values of Ce-TZP-comp implants suggest a reliable intraoral clinical application in the anterior jaw regions.