Development of poly (butylene adipate-co-terephthalate) filled with montmorillonite-polypyrrole for pressure sensor applications

Abstract

A novel pressure sensing material composed of poly (butylene adipate-co-terephthalate) (PBAT) and montmorillonite-polypyrrole (Mt-PPy) was prepared using melt mixing and injection molding. The structure and properties of the PBAT/Mt-PPy composites were evaluated and compared with those of the PBAT/PPy blends. The PBAT/Mt-PPy displays a very sharp insulator-conductor transition and its percolation threshold was reached at 6.5 wt% of Mt-PPy, which was lower than that for PBAT/PPy (11.0 wt% of PPy). The transmission electron microscopy analysis shows that Mt-PPy displays a high aspect ratio and was better distributed and dispersed into PBAT compared to PPy. PBAT/Mt-PPy exhibits a decrease in the electrical resistivity with an applied compressive stress due to the formation of new conducting pathways. The electromechanical response was dependent on Mt-PPy and the maximum sensitivity was observed for the composite containing 10 wt% of Mt-PPy. In this system, the electrical resistivity drops from 9 x 106 to 2 x 106 O cm when a compressive stress of 0.25 MPa was applied. The electrical resistivity changes with applied compressive stress, the reproducibility and the reversibility makes PBAT/Mt-PPy a suitable material for the development of pressure sensors.