Effects of CaO on the compaction and sintering by plasma of Powder-metallurgical iron

Abstract

This work the effect of the addition of Calcium Oxide (CaO) in the compaction and sintering of powder metallurgical iron Ancoor Steel 1000® is studied. Iron samples were made with proportions of: 0.5%, 1%, 1.5% and 2% by weight of CaO. The samples were sintered in a luminescent discharge furnace, in an atmosphere of H2+Ar at a temperature of 1150°C. XRD analysis was used to determine the formation of compounds, this analysis evidenced the formation of: hematite and magnetite, which were found both on the surface and in the volume. A characterization of the ability to protect against corrosive effects was carried out using the EIS electrochemical impedance spectroscopy method on the samples, in a solution of 1000ppm of chloride, with this procedure it was found that at a concentration of 0.5% and 1% CaO, the electrochemical impedance value is increased with values of 11.7M, 2.2M respectively.