Friction behavior of 3D-printed polymeric materials used in sliding systems

Abstract

Recently, 3D-printed polymeric materials have been successfully replacing the usual ones especially used in sliding systems like couplings. Among the polymeric materials, Acrylonitrile Butadiene Styrene (ABS) and Poly Lactic Acid (PLA) can be the competitive materials in such application after 3D-printing. In this study, 3D printing was used to produce samples from ABS and PLA via fused deposition modelling (FDM) technology. Then friction behavior of 3D-printed samples was investigated depending on printing orientation of the samples. Ultra High Molecular Polyethylene Weight (UHMWPE), as a well-known industrial polymer, was also used for comparing the friction behavior of 3D-printed ABS and PLA polymers. Friction tests were conducted using a pin-on-plate type tribometer according to ASTM G133 under different applied loads and sliding speeds at room temperature. It was found that printing orientation of all ABS and PLA samples has a considerable effect on their friction behavior. Transverse direction (T.D) of the 3D-printed samples shows higher coefficient of friction (COF) values than the longitudinal direction under all applied loads and sliding speeds. On the other hand, COF values obtained in both 3D-printed samples increase as the load and speed increase regardless of the printing direction. When both 3D-printed materials are compared, PLA samples exhibit lower COF values than ABS samples in both printing directions and under all loads and speeds. However, the UHMWPE sample produced with traditional method shows much lower COF values and stable change in friction behavior under all conditions compared to 3D-printed PLA and ABS samples.