Synthesis, structural and optical investigations of (Pb, Bi)TiO3 Borosilicate Glasses

Abstract

A new series of lead bismuth titanate borosilicate glasses with addition of one percent lanthanum oxide have been synthesized using melt-quench technique. X-ray diffraction patterns have been recorded to confirm the amorphous nature of the prepared glass samples. The synthesized glasses have been characterized by using various spectroscopic techniques such as UV-visible, infrared, and Raman spectroscopy. UV-visible measurements were recorded in the wavelength range from 200 to 1100 nm whereas IR and Raman spectroscopic measurements were recorded over a continuous wavenumber range from 400 to 5000 cm-1 and 1000 to 2000 cm-1 respectively. The different absorption peaks/bands were formed in IR spectral patterns. The spectral bands appear towards the lower wavenumber sides due to the Bi and Pb, content while the bands appear towards the higher wavenumber sides due to the formation of diborate and triborate network units.