Sifat Listrik Material Ferroelektrik Barium Titanat (BaTiO3) dengan Doping Cerium (Ce)

Abstract

Pembuatan material ferroelektrik Barium Titanat (BaTiO3) didoping cerium (Ce) telah dilakukan. Pemberian variasi komposisi doping dilakukan untuk mengetahui nilai konstanta dielektrik, rugi-rugi dielektrik, tingkat kekeristalan serta ukuran kristal tiap sampel. Sampel dibuat menggunakan metode solid state reaction dengan persentase doping Ce 0%, 1%, 2%, 3%, 4% dan 5% mol yang dikompaksi dalam bentuk pelet. Satelah sampel disintering pada suhu 700°C selama 4 jam, dilakukan karakterisasi menggunakan RLC meter dengan variasi frekuensi 100 Hz, 120 Hz dan 1 KHz dan karakterisasi XRD. Diperoleh hasil bahwa pengaruh doping menaikkan nilai konstanta dielektrik pada komposisi doping 1% mol pada frekuensi 100 Hz dengan nilai konstanta dielektrik sebesar 4220. Pada komposisi  doping 1% ini juga ditemukan nilai faktor desipasi tertinggi yaitu sebesar 4,45. Pada uji XRD ditemukan  komposisi doping 1% memiliki nilai tingkat kekristalan yang lebih besar dari komposisi doping 3% yaitu sebesar 89% Dielectric is a material that is widely developed in technology, especially in applications as capacitors. A study entitledthe effect of the doping composition of cerium (Ce) on barium titanate (BaTiO3) for the dielectric constant and the cyrstal structure ofBa1-xCexTiO3has been conducted. This study aims to determine the effect og giving the doping composition Ce (x=1%, 2%, 3%, 4%, 5%) on BaTiO3, knowing the dissipation factor and the dielectric constant ofBa1-xCexTiO3.The solid state reaction method wasused in this study by reacted the solids in form of powders at a high temperature 750°C for 4 hours. The RLC meter is used to measure the capacitance and then it is processed and the highest dielectic constant and highest dissipation factor are obtained at the 1% doping composition of 55389,387 with a dissipation factor 2,74. The crystal structure was analyzed using xrd, and the highesst intensity results were in composition at 1% doping and 152,84. The hightest crytallinity formed was 89,11 but the largest crystal size was obtained in composition 3% doping is 36,7549 nm