Electrochemical Corrosion Behavior and the Related Mechanism of Ti3SiC2/Cu Composites in a Strong Acid Environment

Abstract

The electrochemical corrosion behaviors of Ti3SiC2/Cu composites in harsh media including dilute HNO3 and concentrated H2SO4 were studied in detail and the related corrosion mechanisms were explored. Under open-circuit potential, the corrosion resistance of Ti3SiC2/Cu in dilute HNO3 was worse than that in concentrated H2SO4. In dilute HNO3, Ti3SiC2/Cu exhibited a typical passivation character with a narrow passivation interval. During the corrosion process, the dissolution of Cu-Si compounds resulted in the destruction of the passivation layer on the surface. Additionally, with the increasing of the potentials, the oxidation of Cu and Si atoms led to the generation of the oxide film again on the surface. In concentrated H2SO4, the Ti3SiC2/Cu composite was covered by a double-layered passivation layer, which was composed of an internal layer of TiO2 and an external layer of Cu2O and SiO2. This was because Cu diffused into the surface and was oxidized into Cu2O, which formed a denser oxidized film with SiO2. In addition, it was found that Ti3SiC2/Cu has better corrosion resistance in concentrated H2SO4.