STUDY OF VISCOSITY OF AQUEOUS SOLUTIONS OF NATURAL POLYSACCHARIDES

Abstract

One of the steps of synthesis of biodegradable polymers is preparation of an aqueous solution of raw materials. Formulation of biodegradable films with optimum characteristics requires to undertake a separate rheological study of each aqueous solution. An essential parameter in this step is a uniform thickness, which is achieved by means of specified viscosity parameters. Viscosity of solutions depends on many parameters, among which are composition and concentration of components in a solution, solution preparation temperature, pH of the finished medium, and presence of free ions. This article describes studies and results on study of viscosity parameters of aqueous solutions of natural polysaccharides: agar-agar, hydroxypropyl methyl cellulose and carrageenan. For aqueous solutions of carrageenan and hydroxypropyl methylcellulose, viscosity was measured at 25°C. In addition, viscosity parameters were measured for 1.5% hhydroxypropyl methylcellulose solutions at 40°C and 60°C. Depending on the gel formation temperature, viscosity of agar-agar solutions was measured at 50°C or 70°C. According to the results of experiments, it was found that viscosity of 1.0-1.5% hydroxypropyl methylcellulose aqueous solutions is in the range of 8.0-80.0 cP. Heating to 100°C at pH 6 results in irreversible destruction of hydroxypropylmethylcellulose molecules. Aqueous solutions of agar-agar are similar to hydroxypropyl methylcellulose solutions but agar-agar is able to gelate at sufficiently low concentrations (from 0.5%). Viscosity of 3.0- 5.0% carrageenan aqueous solutions varies within a wide range: 1.5-1400.0 cP. Thus, rheological properties allow to adjust viscosity of the process mixture in the production of biodegradable polymers in the desired range and in different directions.