Deformation mechanisms in a fine-grained Udimet 720LI nickel-base superalloy with high volume fractions of γ′ phases

Abstract

Hot-deformation behaviors and mechanisms below γ′ solvus of U720LI with fine-grained microstructure and high volume fractions of γ′ phases were studied. MTS hot-compressed samples under hot-deformation parameters (Temperatures of 1040 °C, 1070 °C, 1100 °C, 1130 °C, strain rates of 0.01 s−1, 0.1 s−1, 0.5 s−1 and strains of 0.11, 0.36, 0.69 and 1.2) were investigated by using multiple microstructural analysis methods, such as transmission electron microscopy (TEM), electron channeling contrast image (ECCI), et al. Rare recovery and recrystallization were observed indicating that other deformation mechanisms might be enhanced during the deformation process. Except for the pinning effect, deformation happened within γ′ phases and also γ′ phase promoted the deformation of the matrix. When the slipping was inhibited by γ′ phases, twinning acted as a deformation mechanism in fine-grained U720LI. Due to the retardation effect of γ′ phases in the early stage of the deformation process, local grain boundary migration took effect. Once grain boundaries crossed γ′ phases, it made recrystallization by strain induced boundary motion(SIBM) easier.