Synthesis and characterization of a pyrochlore solid solution in the Na2O-Bi2O3-TiO2 system

Abstract

The compositional limits of a previously reported (J. Am. Ceram. Soc., 61, 5-8. (1978)) but relatively unstudied sodium-bismuth titanate pyrochlore solid solution are revised and their electrical properties presented. The pyrochlore solid solution we report forms via a different mechanism to that originally reported and occurs in a different location within the Na2O-Bi2O3-TiO2 ternary system. In both cases, relatively large amounts of vacancies are required on the A-sites and on the oxygen sites, similar to that reported for undoped ‘Bi2Ti2O7’ pyrochlore. In contrast to ‘Bi2Ti2O7’, this ternary pyrochlore solid solution can be prepared and ceramics sintered using conventional solid-state methods; however, the processing requires several challenges to be overcome to obtain dense ceramics. This cubic pyrochlore series has low electrical conductivity (and does not exhibit any evidence of oxide-ion conduction) and exhibits relaxor ferroelectric behavior with a broad permittivity maximum of ~100 near room temperature. Variable temperature neutron diffraction data do not provide any conclusive evidence for a phase transition in the pyrochlore solid solution between ~4 and 873 K.