In Situ Study of Surface Morphology Formation Mechanism During Laser Powder Bed Fusion

Abstract

In the laser powder bed fusion (LPBF) process, the surface quality of intermediate layers impacts interlayer bonding and part forming quality. Due to the complex dynamic process inherent in LPBF, current monitoring methods struggle to achieve high-quality in situ online monitoring, which limits the in-depth understanding of the evolution mechanisms of the surface morphology of LPBF intermediate layers. This paper employs an optimized coaxial optical imaging method to monitor key LPBF processes and analyzes the intermediate layer surface morphology evolution mechanism considering heat, force, and mass transfer. Results indicate that LPBF intermediate layer surfaces are influenced by energy density, melt pool behavior, and previous layer morphology, forming complex topological structures. At a low energy density, insufficient powder melting causes balling, extended by subsequent melt pools to form a reticulated structure and local large-scale protrusions. Heat accumulation at a high energy density promotes melt pool expansion, reduces melt track overlap, and effectively eliminates defects from previous layers via remelting, with spatter becoming the main defect. Additionally, the melt pool wettability on the part contours captures external powder, forming unique, overhanging contour protrusions. This paper enhances understanding of LPBF intermediate layer surface morphology formation mechanisms and provides a theoretical basis for optimizing surface quality.