Friction-based recycling: an evaluation of friction extrusion for fabricating Ti-6Al-4 V wire fabricated from machining chip feedstock

Abstract

Titanium and its alloys are used in aviation and automobile industries due to their remarkable strength to weight ratio, but machining loss commonly is high with ~ 80 wt% of the material being converted to scrap. Recycling post-consumer Ti scrap directly into solid bulk products is a potential solution for repurposing valuable material. Further, eliminating fresh Ti sponge during recycling might lead to lower energy and greenhouse gas emissions. In this study, a solid-phase process known as friction extrusion was utilized to recycle Ti-6Al-4 V machining chips into solid wires which could be used as feedstock in additive manufacturing. The friction consolidation technique was first used to convert chips with varying degrees of oxygen content into solid billets for its use as feedstock material in subsequent friction extrusion. The extrudates were fabricated above the beta transition temperature, which was achieved by selecting the rotation rate and feed rate, to process the billets near 1000 °C using a tungsten-lanthana extrusion die. This work presents the first occurrence of friction extruded titanium alloy wires. The effect of friction extrusion on microstructural features, tensile properties, and texture are reported. Overall, the friction extrusion method is capable of directly recycling Ti-6Al-4 V scrap into extruded wire.