Development of zinc-plated regenerator material

Abstract

An effective way to improve the efficiency of a cryocooler is to improve the efficiency of the regenerator. In general, the heat capacity of materials decreases as temperature decreases. Thus, when temperature is below 40 K, lead or bismuth spheres are often used as regenerator materials. However, the pressure drop in a sphere regenerator is much larger than that in a screen regenerator. To overcome this dilemma, Xu et al. reported that cooling performance at the temperature of less than 40 K was improved when using tin-plated screens at the cold end of the regenerator. However, the reliability of tin at low temperatures is still not verified fully because of its phase transition from a normal β phase to an abnormal α phase, which may result in a significant reduction of the mechanical strength. In this paper, a zinc-plated screen is proposed as another potential alternative. A comparison test was performed with a two-stage GM cryocooler by replacing part of the first stage regenerator material, phosphorus bronze screens, with zinc-plated screens. Compared to a regenerator filled with bronze screens, the cooling capacity of the first stage increased by about 11% at 40 K and 60% at 30 K with these zinc-plated screens. The detailed experimental results are reported in this paper.