In vitro evaluation of marginal fit of zirconia-reinforced lithium silicate laminate veneers at two thicknesses using different cad/ cam systems

Abstract

Objective: The purpose of this in vitro study was to evaluate the marginal fit of laminate veneers made of zirconia-reinforced lithium silicate with two thicknesses using different CAD/CAM systems. Material and methods: 42 Laminate veneers milled from zirconia-reinforced lithium silicate were divided into three main groups according to milling machine used into: group X5, laminate veneers fabricated by inLab MCX5 milling machine; group CM, laminate veneers fabricated by Ceramill motion 2 milling machine; and group XL, laminate veneers fabricated by inLab MCXL milling machine. Each group was divided into two subgroups according to veneer thickness into: subgroup I, 0.5 mm thickness laminate veneers and subgroup II, 0.3 mm thickness laminate veneers. The marginal fit was measured using stereomicroscope. The results were tabulated and statistically analyzed using two-way ANOVA test followed by Tukey’s post hoc test. Comparisons of main and simple effects were done utilizing Bonferroni correction. The significance level was set at (p ≤0.05) for all tests. Results: The mean ( ± SD) highest marginal discrepancy was recorded in subgroup CMII at 85.45 ± 1.82 µm while the least mean marginal discrepancy was recorded in subgroup X5I (71.24 ± 2.64 µm). Conclusion: Both thicknesses (0.5 mm thickness and 0.3 mm thickness) and all tested CAD/CAM systems produced zirconia-reinforced lithium silicate laminate veneers with clinically acceptable marginal gaps; however, the closed CAD/ CAM systems produced veneers with superior marginal fit than open systems at 0.3 mm thickness. The CAD/ CAM system with the 5-axis milling machine produced the best marginal fit with 0.5 mm thickness.