Optimisation of the Q-P process parameters for low alloyed steels with 0.2% C

Abstract

In steels which are treated by the quenching and partitioning (Q&P) process, carbon content is one of the crucial parameters because carbon contributes greatly to stabilization of retained austenite and strengthens the material. In the present study, the Q&P process was gradually optimised for two low-alloyed steels with 0.2% carbon content and with and without Cr addition. The results show that the cooling rate, as well as the austenitizing temperature, has a pronounced effect on microstructure evolution. The strength and elongation in the Mn, Si and Cralloyed steel was approx. 900 MPa and more than 30%, respectively.