Water-Based Highly Stretchable PEDOT:PSS/Nonionic WPU Transparent Electrode

Abstract

Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) has the merits of high electrical conductivity and solution processability, and can be dispersed in water. To improve the stretchability of PEDOT:PSS-based transparent electrode films, the intrinsically conducting polymer PEDOT:PSS was blended with highly stretchable nonionic waterborne polyurethane (WPU) and coated on a thermoplastic polyurethane (TPU) film. Nonionic WPU has good compatibility with PEDOT:PSS, without affecting the acidity. WPU undergoes hydrogen bonding and coulombic at-tractions with PEDOT:PSS. With variation of the WPU content, differences in the electrical proper-ties, such as the sheet resistance and mechanical stretchability, of the coated thin films were observed. The film with 2.0 wt% WPU could be stretched to 400% of the electrode surface without damage to the surface of the electrode films. The WPU and TPU films both have a polyester group, which provides good adhesion between the WPU-based transparent electrodes and the TPU substrate films. A stretchable alternating current electroluminescence (ACEL) device was constructed by using the water-based PEDOT:PSS/nonionic WPU composite as both the bottom and top transparent electrodes. The fabricated ACEL remained its initial luminance in the 500% stretched state.