Investigating the Static and Dynamic Mechanical Properties of Fiber-Reinforced Concrete Incorporating Recycled Carbon Fiber and Modified Basic Oxygen Furnace Slag Aggregate

Abstract

This study explores the mechanical behavior of concrete reinforced with recycled carbon fiber (RCF) and incorporating modified basic oxygen furnace slag (MBOF) as a sustainable aggregate. The RCF was recovered from waste carbon fiber-reinforced polymer (CFRP) bicycle rims via microwave-assisted pyrolysis (MAP), while MBOF was produced by water-based treatment of hot BOF slag. The experimental program included compressive, splitting tensile, and flexural strength tests, as well as impact resistance and stress-reversal Split Hopkinson Pressure Bar (SRSHPB) tests. The effects of RCF length (6 mm and 12 mm) on the mechanical performance of MBOF-based concrete were systematically examined. The results demonstrated that incorporating MBOF as aggregate, combined with the addition of RCF, significantly enhanced both static strength and dynamic impact resistance. Compared with fiber-free MBOF concrete, the incorporation of 6 mm and 12 mm RCF increased compressive strength by 3.03% and 13.77%, flexural strength by 14.50% and 19.74%, and splitting tensile strength by 2.60% and 25.84%, respectively. Similarly, the impact number increased by approximately 6.81 and 12.67 times for the 6 mm and 12 mm RCF specimens, respectively, relative to the fiber-free specimen. Furthermore, the SRSHPB test results indicated that MBOF concrete reinforced with 12 mm RCF exhibited greater dynamic compressive strength than that reinforced with 6 mm RCF. Overall, MBOF concrete incorporating 12 mm RCF demonstrated superior performance to its 6 mm counterpart across all evaluated strength parameters. These findings highlight the potential of utilizing metallurgical and composite waste to develop high-performance, sustainable concrete materials.