Characterization of low-density polyethylene and ldpe-based/ethylene-vinyl acetate with medium content of vinyl acetate

Abstract

Low-density polyethylene (LDPE) and ethylene vinyl acetate copolymer (EVA), which are non-polar and polar polymers, are immiscible and form a polyphase system. In this study, LDPE was mixed with 2.5%, 5%, 7.5%, 10%, 12.5% Ethylene-vinyl acetate (EVA-28) with a medium content of vinyl acetate (28% VA), respectively by injection molding machine and LDPE. Tensile strength and flexural strength were tested according to ASTM D638-02 standard and ISO 178 standard. The results showed that adding EVA-28 increased the elongation at break of the LDPE/2.5% EVA, LDPE/5% EVA and LDPE/10% EVA blend samples. In addition, the tensile and flexural strength of the LDPE/EVA blend decreases gradually as the EVA-28 content in the blend increases. The hardness decreases with the increasing EVA-28 content. EVA-28 spherical particles appeared scattered on the surface of the LDPE matrix, in the highest EVA-28 percent sample (12.5% EVA-28), the number of particles appeared to be quite a lot, and was dispersed quite evenly on the surface. The LDPE/EVA-28 blend achieved a higher elongation at the break than LDPE, in which 10% EVA-28 gives the highest elongation at break.