Mechanical and Microstructural Behavior of Mine Gold Tailings Stabilized with Non-Conventional Binders

Abstract

Recent tailing dam failures in Brazil have been attributed to liquefaction. Chemical stabilization offers a promising solution to enhance the strength and stiffness of tailings and mitigate liquefaction potential. This study investigated the mechanical and microstructural behavior of gold mine tailings (GMTs) stabilized using (i) an alkali-activated binder composed of sugar cane bagasse ash (SCBA), hydrated eggshell lime (HEL), and sodium hydroxide (NaOH) and (ii) Portland cement (PC). Drained and undrained triaxial shear tests and scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM-EDS) analyses were performed. Specimens stabilized with Portland cement exhibited a strong strain-softening behavior and the highest strength, with 5.3 MPa under 200 kPa confining pressure compared to 2.3 MPa for alkali-activated samples and 740 kPa for untreated GMTs. The addition of either binder also increased both the peak effective friction angle and the critical state stress ratio, confirming an enhanced shear strength. SEM-EDS analyses confirmed the formation of cementitious reaction products, explaining these improvements. This research validates both binders as viable solutions for tailing stabilization, with the novel alkali-activated binder offering a sustainable alternative for large-scale applications.