High quality Y3Al5O12 doped transparent ceramics for laser applications, role of sintering additives

Abstract

SiO2, ZrO2, B2O3 and MgO oxides and their combinations were used as sintering aids for preparation of yttrium aluminum garnet (YAG) ceramics doped by Nd2O3, Er2O3, Ho2O3, Tm2O3 and Yb2O3. The influence of these additives on optimal sintering temperature, grain growth, volume of residual pores and optical quality of the ceramics were investigated. The best combination of the sintering additives was found and high quality samples of YAG:Nd (1 at.%) ceramics were obtained. The original method of laser optical quality characterization of ceramics was developed and tested. The main laser parameters of YAG:Nd (1 at.%) ceramics samples are measured and compared with the best well known laser ceramics. The samples of YAG:RE (RE- Er2O3, Ho2O3, Tm2O3 and Yb2O3) ceramics are obtained, and their optical transmittance spectra are measured. Composite structures of YAG:Yb (5 at.%) - YAG were obtained by the simplest method of successive joint compaction of different composition layers.