TEM characterization of catalyst- and mask-free grown GaN nanorods

Abstract

Catalyst- and mask-free grown GaN nanorods have been investigated using transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM) and energy filtered transmission electron microscopy (EFTEM). The nanorods were grown on nitridated r-plane sapphire substrates in a molecular beam epitaxy reactor. We investigated samples directly after the nitridation and after the overgrowth of the structure with GaN. High resolution transmission electron microscopy (HRTEM) and EFTEM revealed that AlN islands have formed due to nitridation. After overgrowth, the AlN islands could not be observed any more, neither by EFTEM nor by Z-contrast imaging. Instead, a smooth layer consisting of AlGaN was found. The investigation of the overgrown sample revealed that an a-plane GaN layer and GaN nanorods on top of the a-plane GaN have formed. The nanorods reduced from top of the a-plane GaN towards the a-plane GaN/sapphire interface suggesting that the nanorods originate at the AlN islands found after nitridation. However, this could not be shown unambiguously. The number of threading dislocations in the nanorods was very low. The analysis of the epitaxial relationship to the a-plane GaN showed that the nanorods grew along the [000-1] direction, and the [1-100] direction of the rods was parallel to the [0001] direction of the a-plane GaN. © 2010 IOP Publishing Ltd.