Thermoluminescence and Photoluminescence Study of Erbium Doped CaY 2 O 4 Phosphor

  • Dubey V
  • Tiwari R
  • Tamrakar R
  • et al.
N/ACitations
Citations of this article
12Readers
Mendeley users who have this article in their library.

This article is free to access.

Abstract

Phosphor doped with erbium ion with variable concentration (0.5–2 mol%) was synthesized by solid state reaction method. CaY 2 O 4 :Er 3+ phosphor is characterized by X-ray diffraction technique for structural analysis and crystallite size calculation. Average crystallite size was found to be nearly 58 nm. Two prominent TL glow peaks found at 163°C associated with higher temperature peak 340°C. The peak intensity of higher temperature (340°C) peak was less as compared to lower temperature peak (163°C) because the deep trapping formation is less in case of UV irradiation. Sample shows good TL glow curve and for variable UV exposure time maximum TL intensity was found at 20 min UV exposure which is optimized UV exposure time. Sample was studied by photoluminescence emission spectra excited by xenon flash lamp with nearly 360 nm and four prominent peaks found at wavelengths 445, 525, 553, and 565 nm; here the 445 and 565 nm peak were intense as compared to others. From the PL emission spectra, it is concluded that the color tenability of prepared CaY 2 O 4 :Er 3+ was blue-green and it is verified by CIE coordinate. Kinetic parameters of prepared phosphor were calculated by computerized glow curve deconvolution (CGCD) technique.

Cite

CITATION STYLE

APA

Dubey, V., Tiwari, R., Tamrakar, R. K., Markande, C., Rathore, G. S., & Pradhan, M. K. (2015). Thermoluminescence and Photoluminescence Study of Erbium Doped CaY 2 O 4 Phosphor. Indian Journal of Materials Science, 2015, 1–5. https://doi.org/10.1155/2015/745052

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free