Effect of Diel Cycling Temperature, Relative Humidity, and Synthetic Route on the Surface Morphology and Hydrolysis of α-U3O8

6Citations
Citations of this article
7Readers
Mendeley users who have this article in their library.

This article is free to access.

Abstract

The speciation and morphological changes of α-U3O8 following aging under diel cycling temperature and relative humidity (RH) have been examined. This work advances the knowledge of U-oxide hydration as a result of synthetic route and environmental conditions, ultimately giving novel insight into nuclear material provenance. α-U3O8 was synthesized via the washed uranyl peroxide (UO4) and ammonium uranyl carbonate (AUC) synthetic routes to produce unaged starting materials with different morphologies. α-U3O8 from UO4 is comprised of subrounded particles, while α-U3O8 from AUC contains blocky, porous particles approximately an order of magnitude larger than particles from UO4. For aging, a humidity chamber was programmed for continuous daily cycles of 12 "high"hours of 45 °C and 90% RH, and 12 "low"hours of 25 °C and 20% RH. Samples were analyzed at varying intervals of 14, 24, 36, 43, and 54 days. At each aging interval, crystallographic changes were measured via powder X-ray diffraction coupled with whole pattern fitting for quantitative analysis. Morphologic effects were studied via scanning electron microscopy and 12-way classification via machine learning. While all samples were found to have distinguishing morphologic characteristics (93.2% classification accuracy), α-U3O8 from UO4 had more apparent change with increasing aging time. Nonetheless, α-U3O8 from AUC was found to hydrate more quickly than α-U3O8 from UO4, which can likely be attributed to its larger surface area and porous starting material morphology.

Cite

CITATION STYLE

APA

Hanson, A. B., Nizinski, C. A., & McDonald, L. W. (2021). Effect of Diel Cycling Temperature, Relative Humidity, and Synthetic Route on the Surface Morphology and Hydrolysis of α-U3O8. ACS Omega, 6(28), 18426–18433. https://doi.org/10.1021/acsomega.1c02487

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free