Attempts to improve the subsurface properties of horizontally-formed cementitious composites using tin(ii) fluoride nanoparticles

Abstract

This article presents studies that were performed in order to improve the subsurface properties of horizontally-formed cementitious composites using tin(II) fluoride nanoparticles. The main aim of the study was to solve the problem of the decrease in subsurface properties caused by mortar bleeding and the segregation of the aggregate along the height of the overlay. The article also aims to highlight the patch grabbing difficulties that occur during the process of forming horizontally-formed cementitious composites. Four specimens were analyzed: one reference sample and three samples modified with the addition of 0.5, 1.0, and 1.5% of tin(II) fluoride nanoparticles in relation to the cement mass. To analyze the mechanical properties of the specimens, non-destructive (ultrasonic pulse velocity) and destructive tests (flexural tensile strength, compressive strength, abrasion resistance, pull-off strength) were performed. It was indicated that due to the addition of the tin(II) fluoride, it was possible to enhance the subsurface tensile strength and abrasion resistance of the tested cementitious composites. To confirm the obtained macroscopic results, the porosity of the subsurface was measured using SEM. It was also shown that the addition of the tin(II) fluoride nanoparticles did not reduce its flexural and compressive strength. The results show that horizontally-formed cementitious composites with the addition of 1.0% of tin(II) fluoride nanoparticles in relation to the cement mass obtained the most effective mechanical performance, especially with regard to subsurface properties.