Effects of Temperature, Stress, and Grain Size on the High-Temperature Creep Mechanism of FeCrAl Alloys

Abstract

FeCrAl exhibits excellent resistance to high temperatures, corrosion, and irradiation, making it a prime candidate material for accident-tolerant fuel (ATF) cladding. This study investigates the high-temperature creep behavior of FeCrAl alloys with grain sizes of 12.0 μm and 9.9 μm under temperatures ranging from 450 °C to 650 °C and applied stresses between 75 and 200 MPa. The texture, grain morphology, grain orientation, and dislocation density of FeCrAl were characterized by electron backscatter diffraction (EBSD). The results indicate that temperature, applied stress, and grain size are the primary factors governing high-temperature creep behavior. The material texture showed no significant difference before and after creep. Large grains tend to engulf smaller ones during the creep process at lower temperatures and stresses, reducing the proportion of low-angle grain boundaries (LAGBs). In contrast, at higher temperatures or under higher stress, dislocations proliferate within grains, leading to a significant increase in the number of LAGBs. As the applied stress increases, the dominant creep mechanism tends to convert from grain boundary sliding to dislocation motion. Moreover, higher temperatures or smaller grain sizes lower the critical stress required to activate dislocation motion and significantly increase dislocation density, severely degrading the creep resistance.