Formation of Self-Healing Organic Coatings for Corrosion Protection of Al Alloys by Dispersion of Spherical and Fibrous Capsules

Abstract

In previous works, we developed a self-healing organic coating with dispersed spherical capsules for corrosion protection. The capsule consisted of a polyurethane shell and healing agent as the inner. When the coating was damaged physically, the capsules were broken, and the healing agent was released from the broken capsules to the damaged area. The healing agent could react with moisture in the air to form the self-healing structure and cover the damaged area of coating. In the present investigation, a self-healing organic coating with spherical and fibrous capsules was formed on aluminum alloys. The corrosion behavior of the specimen coated with the self-healing coating was examined in a Cu2+/Cl− solution after physical damage, and it was found that no corrosion occurred during the corrosion test. This is discussed in terms of the high healing ability of fibrous capsules as a result of the high projected area.