Effects of Au and Ge additions on the microstructures and properties of Ag-1.5Cu-0.1Y alloys

Abstract

The application of silver is seriously affected by its tendency to oxidize and corrode. Therefore, the addition of proper alloying elements to silver-based alloys to achieve better properties has become a hot topic at present. In this current study, the effects of the addition of the two elements Au and Ge on the microstructures and properties of Ag-1.5Cu-0.1Y alloys were investigated. The results showed that the microstructures were refined and the second dendrite was shortened in the Ag-1.5Cu-0.1Y alloys with the addition of Au and Ge. Adding Au enhanced the corrosion resistance of the Ag-1.5Cu-0.1Y alloys. Furthermore, the corrosion resistance of the Ag-1.5Cu-0.1Y alloys with the addition of both Ge and Au was better than that of the alloy samples with Au added alone. The best corrosion resistance of the Ag-1.5Cu-0.1Y alloys was achieved by adding 1.0 wt.% Au and 1.0 wt.% Ge. The microhardness was enhanced by the addition of Au and Ge, and was strongly correlated with the secondary dendrite arm spacing (λ 2 ) of the Ag-1.5Cu-0.1Y alloys. In addition, the Au addition could improve the conductivity of the Ag-1.5Cu-0.1Y alloy; however, Ge had little effect on the conductivity of the alloy samples. This work provides an experimental basis for the design of better performing silver-based alloys.