Wear‐accelerated corrosion of Ti‐6Al‐4V and nitrogen‐ion‐implanted Ti‐6Al‐4V: Mechanisms and influence of fixed‐stress magnitude

Abstract

Wear‐accelerated corrosion rates at constant anodic potentials were evaluated for unimplanted and nitrogen‐ion‐implanted surgical Ti‐6Al‐4V while wearing against ultrahigh‐molecular‐weight polyethylene at stress levels up to 6.90 MPa (1000 psi). The ion implantation processing was found to reduce the wear corrosion rates in both saline and serum solutions at all applied stress levels. During wear testing, all of the ion‐implanted surfaces remained visually unchanged from the polished condition. However, many of the unimplanted surfaces developed damage zones characterized by wear tracks and black wear debris. A surface‐damage mechanism is proposed and discussed which involves disruption of the Ti‐6Al‐4V protective oxide film, subsequent entrapment of oxide particles in the polyethylene, then self‐perpetuating damage due to the abrasive action of the embedded particles. Copyright © 1987 John Wiley & Sons, Inc.