Aluminum melt filtration with carbon bonded alumina filters

Abstract

The wetting behavior was measured for Al2O3-C in contact with AlSi7Mg with a conventional sessile drop test (vacuum, 950 °C and 180 min) and a sessile drop test with a capillary purification unit (vacuum, 730 °C and 30 min). The conventional test yielded contact angles of around 92ffi, whereas the sessile drop measurement with capillary purification showed a strongly non-wetting behavior with a determined apparent contact angle of the rolling drop of 157ffi. Filtration tests, which were repeated twice, showed that the Al2O3-C filter possessed a better filtration behavior than the Al2O3 reference filter. For both filtration trials, the PoDFA (porous disc filtration analysis) index of the Al2O3-C filter sample was equal to half of the PoDFA index of the Al2O3 reference filter sample, indicating a significantly improved filtration performance when using Al2O3-C filter. Notable is the observation of a newly formed layer between the aluminum and the Al2O3-C coating. The layer possessed a thickness between 10 μm up to 50 μm and consisted of Al, C, and O, however, with different ratios than the original Al2O3-C coating. Thermodynamic calculations based on parameters of the wetting and filtration trials underline the possible formation of an Al4O4C-layer.