Reactivity of Cu with poly(tetrafluoroethylene) and poly(vinyl chloride): Effect of pre- and post-metallization modification on the metal/polymer interface

Abstract

The reactivity of Cu with poly(tetrafluoroethylene) (PTFE) and poly(vinylchloride) (PVC) during thermal evaporation, as well as the effect of pre- and post-metallization Ar+ ion and x-ray mediated surface modification treatments on the metal/polymer interface, have been studied using in situ x-ray photoelectron spectroscopy (XPS) and ex situ atomic force microscopy (AFM). During thermal evaporation, copper was unreactive on PTFE but reacted with PVC to form CuCl. Pretreatment of PTFE or PVC surfaces by Ar+ ion or x-ray irradiation did not modify the chemical reactivity of the polymer surface during subsequent Cu deposition, although significant morphological changes were observed on PTFE by AFM. In contrast, post-metallization modification of the Cu/PTFE interface by Ar+ ion or x-ray irradiation lead to the production of CuF2, and increased the yield of CuCl in the Cu/PVC system. In either the Cu/PTFE or Cu/PVC systems, the maximum concentration of copper halide formed and dependence upon treatment time was found to be similar for either Ar+ ion or x-ray irradiation post-metallization treatment strategies, suggesting a common reaction mechanism.