Alloying a single and a double perovskite: a Cu +/2+ mixed-valence layered halide perovskite with strong optical absorption

Abstract

A novel 2D halide perovskite with stoichiometric quantities of Cu + , Cu 2+ , and In 3+ in the inorganic slabs shows emergent properties not seen in Cu II or Cu I –In III perovskites, including enhanced visible-light absorption and electronic conductivity. Introducing heterovalent cations at the octahedral sites of halide perovskites can substantially change their optoelectronic properties. Yet, in most cases, only small amounts of such metals can be incorporated as impurities into the three-dimensional lattice. Here, we exploit the greater structural flexibility of the two-dimensional (2D) perovskite framework to place three distinct stoichiometric cations in the octahedral sites. The new layered perovskites AI4[Cu II (Cu I In III ) 0.5 Cl 8 ] ( 1 , A = organic cation) may be derived from a Cu I –In III double perovskite by replacing half of the octahedral metal sites with Cu 2+ . Electron paramagnetic resonance and X-ray absorption spectroscopy confirm the presence of Cu 2+ in 1 . Crystallographic studies demonstrate that 1 represents an averaging of the Cu I –In III double perovskite and Cu II single perovskite structures. However, whereas the highly insulating Cu I –In III and Cu II perovskites are colorless and yellow, respectively, 1 is black, with substantially higher electronic conductivity than that of either endmember. We trace these emergent properties in 1 to intervalence charge transfer between the mixed-valence Cu centers. We further propose a tiling model to describe how the Cu + , Cu 2+ , and In 3+ coordination spheres can pack most favorably into a 2D perovskite lattice, which explains the unusual 1 : 2 : 1 ratio of these cations found in 1 . Magnetic susceptibility data of 1 further corroborate this packing model. The emergence of enhanced visible light absorption and electronic conductivity in 1 demonstrates the importance of devising strategies for increasing the compositional complexity of halide perovskites.