Investigation of mechanical and magnetic properties of co-based amorphous powders obtained by atomization

Abstract

Properties of Co-based alloys with high Glass Forming Ability (GFA) in the form of powder are still not widely known. However, powders of high GFA alloys are often used for the development of bulk metallic glasses by additive manufacturing. In this work Co47.6B21.9Fe20.4Si5.1Nb5% at. and Co42B26.5Fe20Ta5.5Si5Cu1% at. were developed by gas-atomization. Obtained powders in size 50– 80 µm were annealed at Tg and Tx of each alloy. Then SEM observation, EDS analyses, differential thermal analysis, X-ray diffraction, nanoindentation, Mössbauer, and magnetic properties research was carried out for as-atomized and annealed states. The gas atomization method proved to be an efficient method for manufacturing Co-based metallic glasses. The obtained powder particles were spherical and chemically homogeneous. Annealing resulted in an increase of mechanical properties such as hardness and the elastic module of Co47.6B21.9Fe20.4Si5.1Nb5% at and Co42B26.5Fe20Ta5.5Si5Cu1%, which was caused by crystallization. The magnetic study shows that Co47.6B21.9Fe20.4Si5.1Nb5 and Co42B26.5Fe20Ta5.5Si5Cu1 are soft magnetic and semi-hard magnetic materials, respectively.