Differential Corrosion Behavior of High-Aluminum 304 Stainless Steel in Molten Nitrate Salts: The Roles of Rolling and Heat Treatment

Abstract

The high material cost has restricted the development of concentrated solar power (CSP) systems. In this study, a low-cost alternative material was developed by adding aluminum to 304 stainless steel to form a protective oxide film, thereby enhancing its corrosion resistance to molten salt. Three material variants were tested: untreated hot-rolled plates after solution treatment and cold-rolled high-aluminum 304 stainless steel (High-Al304SS) after solution treatment and annealing treatment. After all samples were immersed in a NaNO3-KNO3 mixed salt at 600 °C for 480 h, corrosion products including NaFeO2, CrO2, Mn2O4, and NiCr2O4 were formed. The phase composition was determined by XRD, and the surface and cross-section of the corrosion layer were analyzed by SEM and EDS surface and point analysis. The corrosion rate of the samples was calculated by the weight loss method. Notably, an Al2O3-Cr2O3 composite oxide film was formed on the sample surface, effectively inhibiting corrosion. The high defect density and grain boundary energy introduced by the cold-rolling process, as well as the precipitation of the second phase during annealing, accelerated the corrosion process of the samples. However, the hot-rolled samples after solution treatment exhibited excellent corrosion resistance (64.43 μm/year) and, through further process optimization, are expected to become an ideal low-cost alternative material for 347H stainless steel (23 μm/year) in CSP systems.