Preferential protection of low coordinated sites in pt nanoparticles for enhancing durability of pt/c catalyst

Abstract

Protecting low coordinated sites (LCS) of Pt nanoparticles, which are vulnerable to dis-solution, may be an ideal solution for enhancing the durability of polymer electrolyte fuel cells (PEMFCs). However, the selective protection of LCSs without deactivating the other sites presents a key challenge. Herein, we report the preferential protection of LCSs with a thiol derivative having a silane functional group, (3-mercaptopropyl) triethoxysilane (MPTES). MPTES preferentially adsorbs on the LCSs and is converted to a silica framework, providing robust masking of the LCSs. With the preferential protection, the initial oxygen reduction reaction (ORR) activity is marginally reduced by 8% in spite of the initial electrochemical surface area (ECSA) loss of 30%. The protected Pt/C catalyst shows an ECSA loss of 5.6% and an ORR half-wave potential loss of 5 mV after 30,000 voltage cycles between 0.6 and 1.0 V, corresponding to a 6.7-and 2.6-fold durability improvement compared to unprotected Pt/C, respectively. The preferential protection of the vulnerable LCSs provides a practical solution for PEMFC stability due to its simplicity and high efficacy.