Structural properties and magnetic interactions in Al3+ and Cr3+ co-substituted CoFe2O4 ferrite

Abstract

A series of CoAlxCrxFe2-2xO4 systems (x = 0.1 to 0.5 in steps of x = 0.1) spinel ferrites have been synthesized successfully using wet chemical co-precipitation technique. The samples were characterized by X-ray diffraction (XRD), infrared spectroscopy (IR) and magnetization measurements. The powder XRD patterns confirm the single phase spinel structure for the materials synthesized. X -ray diffraction measurements were performed to yield the lattice constant as function of the amount x corresponding to Al-Cr substitution. Lattice parameters, X-ray density, bulk density and particle size decrease whereas porosity increases with the increase in Al-Cr content, 'x'. Infrared studies show two absorption bands at about 400 cm-1 and 600 cm-1 for octahedral and tetrahedral sites, respectively. Saturation magnetization decreases with the increase in Al-Cr content x. AC magnetic susceptibility measurements were carried out as a function of temperature to measure the Curie temperature, which was found to decrease with Al-Cr content x. The decrease of Curie temperature has been explained by A-B interaction. © 2010 Versita Warsaw and Springer-Verlag Wien.